2.78 G/Cc Density Seamless Aluminum Round Pipe High Corrosion Resistance 2024 T3

Place of Origin china
Brand Name HUANYU
Model Number HYRT2024T3
Minimum Order Quantity 1 metric tons
Price Negotiable
Packaging Details Plywood Case
Delivery Time 40 days
Payment Terms T/T
Supply Ability 50 Metric Tons Per Month
Product Details
Density 2.78 G/cc Ultimate Tensile Strength 186 MPa
Tensile Yield Strength 75.8 MPa Hardness, Brinell 47
Elongation At Break (Typical; 1/2 In. (12.7 Mm) Diameter) 22 % Melting Point 502 - 638 Degrees C
Annealing Temperature 413 Degrees C Solution Temperature 256 Degrees C
High Light

aluminum alloy pipe

,

aluminum tube pipe

Leave a Message
Product Description

High Corrosion Resistance 2024 T3 Seamless Aluminum Round Tubing

2024 seamless aluminum tubing

2024T3 round tubing has high strength and excellent fatigue resistance which is used to advantage on structures and parts where a good strength-to-weight ratio is desired

 

 

 

Physical Properties

  Metric English Comments
 
Density 2.78 g/cc 0.1 lb/in³ AA; Typical

Mechanical Properties
 
Hardness, Brinell 47 47 AA; Typical; 500 g load; 10 mm ball
Ultimate Tensile Strength 186 MPa 27000 psi AA; Typical
Tensile Yield Strength 75.8 MPa 11000 psi AA; Typical
Elongation at Break 20 % 20 % AA; Typical; 1/16 in. (1.6 mm) Thickness
Elongation at Break 22 % 22 % AA; Typical; 1/2 in. (12.7 mm) Diameter
Modulus of Elasticity 73.1 GPa 10600 ksi AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus.
Ultimate Bearing Strength 345 MPa 50000 psi Edge distance/pin diameter = 2.0
Bearing Yield Strength 131 MPa 19000 psi Edge distance/pin diameter = 2.0
Poisson's Ratio 0.33 0.33  
Fatigue Strength 89.6 MPa 13000 psi AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen
Machinability 30 % 30 % 0-100 Scale of Aluminum Alloys
Shear Modulus 28 GPa 4060 ksi  
Shear Strength 124 MPa 18000 psi AA; Typical

Electrical Properties
 
Electrical Resistivity 3.49e-006 ohm-cm 3.49e-006 ohm-cm AA; Typical at 68 Degrees F

Thermal Properties
 
CTE, linear 68 Degrees F 23.2 µm/m- Degrees C 12.9 µin/in- Degrees F AA; Typical; Average over 68-212 Degrees F range.
CTE, linear 250 Degrees C 24.7 µm/m- Degrees C 13.7 µin/in- Degrees F Average over the range 20-300 Degrees C
Heat Capacity 0.875 J/g- Degrees C 0.209 BTU/lb- Degrees F  
Thermal Conductivity 193 W/m-K 1340 BTU-in/hr-ft²- Degrees F AA; Typical at 77 Degrees F
Melting Point 502 - 638 Degrees C 935 - 1180 Degrees F AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater. Eutectic melting is not eliminated by homogenization.
Solidus 502 Degrees C 935 Degrees F AA; Typical
Liquidus 638 Degrees C 1180 Degrees F AA; Typical

Processing Properties
 
Annealing Temperature 413 Degrees C 775 Degrees F  
Solution Temperature 256 Degrees C 493 Degrees F

 

 

2.78 G/Cc Density Seamless Aluminum Round Pipe High Corrosion Resistance 2024 T3 0